Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation./
作者:	Ghods, Masoud.
出版者:	Ann Arbor : ProQuest Dissertations & Theses, : 2017,
面頁冊數:	117 p.
附註:	Source: Dissertation Abstracts International, Volume: 79-01(E), Section: B.
Contained By:	Dissertation Abstracts International79-01B(E).
標題:	Chemical engineering. -
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10645622
ISBN:	9780355186536

Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation.
Ghods, Masoud.

Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation. - Ann Arbor : ProQuest Dissertations & Theses, 2017 - 117 p.

Source: Dissertation Abstracts International, Volume: 79-01(E), Section: B.

Thesis (D.Engr.)--Cleveland State University, 2017.

This dissertation explores the role of different types of convection on macrosegregation and on dendritic array morphology of two aluminum alloys directionally solidified through cylindrical graphite molds having both cross-section decrease and increase. Al- 19 wt. % Cu and Al-7 wt. % Si alloys were directionally solidified at two growth speed of 10 and 29.1 mum s-1 and examined for longitudinal and radial macrosegregation, and for primary dendrite spacing and dendrite trunk diameter.

ISBN: 9780355186536Subjects--Topical Terms:

560457
Chemical engineering.

Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation.
LDR:04312nmm a2200445 4500 001 2160492
005 20180727091503.5
008 190424s2017 ||||||||||||||||| ||eng d
020 $a 9780355186536
035 $a (MiAaPQ)AAI10645622
035 $a (MiAaPQ)OhioLINK:csu1500217305972883
035 $a AAI10645622
040 $a MiAaPQ $c MiAaPQ
100 1 $a Ghods, Masoud. $3 3348414
245 1 0 $a Effect of Convection Associated with Cross-section Change during Directional Solidification of Binary Alloys on Dendritic Array Morphology and Macrosegregation.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2017
300 $a 117 p.
500 $a Source: Dissertation Abstracts International, Volume: 79-01(E), Section: B.
500 $a Adviser: Surendra Tewari.
502 $a Thesis (D.Engr.)--Cleveland State University, 2017.
520 $a This dissertation explores the role of different types of convection on macrosegregation and on dendritic array morphology of two aluminum alloys directionally solidified through cylindrical graphite molds having both cross-section decrease and increase. Al- 19 wt. % Cu and Al-7 wt. % Si alloys were directionally solidified at two growth speed of 10 and 29.1 mum s-1 and examined for longitudinal and radial macrosegregation, and for primary dendrite spacing and dendrite trunk diameter.
520 $a Directional solidification of these alloys through constant cross-section showed clustering of primary dendrites and parabolic-shaped radial macrosegregation profile, indicative of "steepling convection" in the mushy-zone. The degree of radial macrosegregation increased with decreased growth speed. The Al- 19 wt. % Cu samples, grown under similar conditions as Al-7 wt. % Si, showed more radial macrosegregation because of more intense "stepling convection" caused by their one order of magnitude larger coefficient of solutal expansion.
520 $a Positive macrosegregation right before, followed by negative macrosegregation right after an abrupt cross-section decrease (from 9.5 mm diameter to 3.2 mm diameter), were observed in both alloys; this is because of the combined effect of thermosolutal convection and area-change-driven shrinkage flow in the contraction region. The degree of macrosegregation was found to be higher in the Al- 19 wt. % Cu samples. Strong area-change-driven shrinkage flow changes the parabolic-shape radial macrosegregation in the larger diameter section before contraction to "S-shaped" profile. But in the smaller diameter section after the contraction very low degree of radial macrosegregation was found.
520 $a The samples solidified through an abrupt cross-section increase (from 3.2 mm diameter to 9.5 mm diameter) showed negative macrosegregation right after the cross-section increase on the expansion platform. During the transition to steady-state after the expansion, radial macrosegregation profile in locations close to the expansion was found to be "S-shaped". This is attributed to the redistribution of solute-rich liquid ahead of the mushy-zone as it transitions from the narrow portion below into the large diameter portion above.
520 $a Solutal remelting and fragmentation of dendrite branches, and floating of these fragmented pieces appear to be responsible for spurious grains formation in Al- 19 wt. % Cu samples after the cross-section expansion. New grain formation was not observed in Al-7 wt. % Si in similar locations; it is believed that this is due to the sinking of the fragmented dendrite branches in this alloy.
520 $a Experimentally observed radial and axial macrosegregations agree well with the results obtained from the numerical simulations carried out by Dr. Mark Lauer and Prof. David R. Poirier at the University of Arizona.
520 $a Trunk Diameter (TD) of dendritic array appears to respond more readily to the changing growth conditions as compared to the Nearest Neighbor Spacing (NNS) of primary dendrites.
590 $a School code: 0466.
650 4 $a Chemical engineering. $3 560457
650 4 $a Physics. $3 516296
650 4 $a Condensed matter physics. $3 3173567
650 4 $a Materials science. $3 543314
650 4 $a High temperature physics. $3 3192580
650 4 $a Automotive engineering. $3 2181195
650 4 $a Engineering. $3 586835
650 4 $a Aerospace engineering. $3 1002622
690 $a 0542
690 $a 0605
690 $a 0611
690 $a 0794
690 $a 0597
690 $a 0540
690 $a 0537
690 $a 0538
710 2 $a Cleveland State University. $b Washkewicz College of Engineering. $3 3348415
773 0 $t Dissertation Abstracts International $g 79-01B(E).
790 $a 0466
791 $a D.Engr.
792 $a 2017
793 $a English
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10645622